Année | Atelier | Nb. de Frappe | Métal | Diamètre | Poids - Masse | Epaisseur | Graveur |
1850 | s.m.A | 11 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1851 | s.m.A | (avec 1850) | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1866 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1870 | s.m.B | 540 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1875 | s.m.B | 984 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1879 | s.m.B | 990 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1883 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1886 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1888 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1890 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1893 | s.m.B | 2 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1896 | s.m.B | 20 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1897 | s.m.B | 487 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1898 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1899 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1900 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1902 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1903 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1904 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1906 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1907 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1908 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1909 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1910 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1912 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1913 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1914 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1915 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1918 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1919 | s.m.B | 2 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1920 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1925 | s.m.B | 1 250 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1926 | s.m.B | 750 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1927 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1928 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1929 | s.m.B | 750 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1930 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1931 | s.m.B | 1 288 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1932 | s.m.B | 1 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1933 | s.m.B | 1 000 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1934 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1936 | s.m.B | 500 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1937 | s.m.B | 1 200 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1938 | s.m.B | 1 369 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |
1941 | s.m.B | 3 448 000 | Bronze (Cu 95 % – Sn 4 % – Zn 1 %) | 20 mm. | 2.5 gr. | 1.4 mm. | Jean-Jacques Barre |